Polymaker Fiberon PA6-CF20 Carbon Fiber Nylon Filament 1.75mm, Black, 0.5kg
5 sold in last 24 hours
- 20% Carbon Fiber Reinforced PA6: Fiberon PA6-CF20 combines Nylon 6 with 20% carbon fiber for high stiffness, strength, dimensional stability, and strong layer adhesion. Designed for rigid functional parts, tooling, fixtures, and automotive or industrial prototypes.
- Engineering Performance After Annealing: Typical TDS values include 109.3 MPa dry X-Y tensile strength and an 8.64 GPa Young’s modulus. Heat deflection temperature reaches 215°C at 0.45 MPa after annealing at 100°C for 16 hours. Final-part performance may vary with design and printing conditions.
- Dry Before and During Printing: PA6 is moisture-sensitive. Dry the filament at 100°C for 10 hours before printing, then store and print below 20% relative humidity, ideally from a dry box. Proper moisture control helps reduce stringing, bubbles, rough surfaces, and inconsistent extrusion.
- Advanced Printer Setup Required: Use a 280–300°C nozzle, a 40–50°C build plate, and an all-metal hotend with the cooling fan off. A heated chamber is not required; room-temperature chamber conditions are listed in the TDS. Printing speeds up to 300 mm/s are possible with a properly tuned profile.
- Use a Wear-Resistant Nozzle: Carbon fiber is abrasive, so a hardened steel or ruby nozzle is required instead of a standard brass nozzle. For optimum heat resistance and dimensional stability, anneal printed parts at 100°C for 16 hours. Before long prints, confirm smooth filament routing and unrestricted spool rotation.
Estimated shipping
Select a product to estimate shipping.Filament PA6-CF 20%
Fiberon PA6-CF20
3D printing filament
HDT(°C) @0.45 MPa: 215
Bending modulus (dry-MPa): 7037
Bending modulus (wet-MPa): 2286
Product details
| Main Specification | |
|---|---|
| Fabricant | Polymaker |
| Numéro d'unité | 17.64 Ounce |
| Marque | Polymaker |
| Nombre d'articles | 1 |
| Diamètre de l'article | 1,75 millimètres |
| Couleur | Black Pa6-cf20 |
| Numéro d'identification du commerce mondial | 06938936714613 |
| Poids de l'article | 0,5 kg |
| Product information | |
| Nombre d ' emballages | 1 |
| Technical Details | |
| Numéro de pièce du fabricant | FG03001 |
| Type de matériau | Nylon |
| Item details | |
| Numéro de modèle | FG03001 |
| Features & Specs | |
| Caractéristiques supplémentaires | Carbon Fiber Reinforcement for Enhanced Strength and Heat Resistance |
| Others | |
| Point en évidence | 20% Carbon Fiber Reinforced PA6 Filament or High-Strength Heat-Resistant PA6-CF Engineering 3D Printer Material |
| Type de produit | Filament d'impression 3D |